Silicone seals for gaskets

详情

Product Information

Double Component Silicone Adhesive
KL**1(A/B)
KL**1A/B two component adhesive at high temperature curing condition. Excellent and durable
adhesion with many kinds of materials after cured. The raw materials are characterized good
flowing ability before curing and the better electrical insulating property after cured.
Application:
Applied to silicone bonding with silicone to have insulation proof,moisture proof, shock
absorption and sealing function.
Physical Properties：
Before curing：
Mix viscosity(*5℃)，mΡa.s: ****0
Specific Gravity(g/cm³): 1.*0
Operable time(*5℃),h: 4.0
Curing time（*0℃）,min.: ***0
After curing:
Tensile strength(Mpa): 4.0
Hardness(Shores A): *5±5
Elongation(%): **0
Adhesive property: ≥2.0(A1A1,cohesive failure )
Volume resistance(Ω • cm): 1×*0
Dielectric strength(KV/mm): *0
Method of application:
• Application ratio: A:B=1:1(weight ratio)
• The adhesive is added by weight ratio and thoroughly mixed.
• Before gluing,the thoroughly mixed adhesive should be degased vacuum degassing,
• Brush the mixture glue onto the surface under the vacuum condition.
• Curing at **0°C for ***5 Seconds.
• Mixed with primer coating(CL*4S3) will make the metal which glued with cured silicone
more viscosity
Shenzhen Kanglibang Science and Technology Co., Ltd.
Product Information


Note：
• Kept in a seal place.
• Curing time and the size of sealant parts accordance with heat transfer efficiency under the
certain temperature.
• Testing compatibility of rubber and base material before using. Because the compound which
contained sulfur, tin,arsenic,phosphorus,nitrogen,PB will cause of bad curing during the curing
process.
Packing:
1kg/Bottle