When Sinoma 3D fiber glass fabric is impregnated with a thermoset
resin, the fabric absorbs the resin and rises to the preset height.
Owing to the integral structure, composites made of 3d sandwich
woven fabric boast superior resistance against delamination to
traditional honeycomb and foam cored materials.
Advantages：
1、Light weight but high strength;
2、Great resistance against delamination;
3、High design-versatility;
4、Space between both decklayers can be multi-functional (embedded
with sensors and wires or infused with foam);
5、Simple and effective lamination process
6、Thermal and sound insulated.; Fire retardant; Wave
transmittable.
| Datasheet of 3D laminates with polyester resin |
| Subjects | Test Method | 2 | 3 | 5 | 8 | *0 | *2 | *5 | *8 | *0 | |
| Thermal Conductivity | DIN ****6(N) | W/mk | 0.*5 | 0.*6 | 0.*6 | 0.*6 | 0.*8 | 0.*8 | 0.*8 | 0.*8 | 0.*8 |
| Thermal Resistance | DIN ****6(N) | ㎡k/w | 0.*4 | 0.*5 | 0.*8 | 0.*2 | 0.*3 | 0.*5 | 0.*8 | 0.*1 | 0.*4 |
| Tensile Strength | ASTM D***9/**9(N) | Mpa | **3 | **2 | **5 | **7 | **4 | **3 | **1 | **2 | **1 |
| **4 | **8 | **6 | **4 | **8 | **2 | **9 | **5 | **8 | |||
| Flatwise Compression | ASTM **5(N) | Mpa | *0.2 | 8.7 | 5.1 | 4.5 | 2.6 | 2.4 | 2.2 | 1.9 | 1.3 |
| 8.9 | 7.5 | 3.9 | 3.1 | 2.3 | 2.0 | 1.9 | 1.4 | 0.9 | |||
| Shear Strength | ASTM **3(N) | Mpa | 3.6 | 3.0 | 2.8 | 2.9 | 2.7 | 2.5 | 2.1 | 1.8 | 1.3 |
| 2.1 | 1.7 | 1.4 | 1.2 | 1.0 | 1.0 | 0.8 | 0.6 | 0.5 | |||
| Shear Modulus | ASTM **3(N) | Mpa | *7 | *3 | *2 | *6 | *7 | *4 | *9 | *1 | *6 |
| *1 | *4 | *1 | *7 | *4 | *1 | *8 | *9 | *8 | |||
| Bending Strength | ASTM **3(N) | Mpa | **4 | **6 | **1 | **7 | **4 | *7 | *2 | *9 | *5 |
| *7 | *1 | *8 | *5 | *2 | *9 | *5 | *7 |
*4 |
| 国家: | China |
| 型号: | 3D fiber glass composite |
| 离岸价格: | 获取最新报价 |
| 位置: | - |
| 最小订单价格: | - |
| 最小订单: | - |
| 包装细节: | - |
| 交货时间: | - |
| 供应能力: | - |
| 付款方式: | - |
| 產品組 : | - |