Hastelloy X is recommended especially for use in furnace
applications because it has unusual resistance to oxidizing,
reducing, and neutral atmospheres. Furnace rolls made of this alloy
were still in good condition after operating for 8,**0 hours at
***0 °F (***7°C).Alloy X also has performed well in jet engine
tailpipes, afterburner components, cabin heaters, and other
aircraft parts.Strong and Oxidation ResistanceHASTELLOY® X alloy is
a nickel-chromium-iron-molybdenum alloy that possesses an
exceptional combination of oxidation resistance, fabricability and
high-temperature strength. It has also been found to be
exceptionally resistant to stress-corrosion cracking in
petrochemical applications. X alloy exhibits good ductility after
prolonged exposure at temperatures of ***0, ***0, ***0°F (**0, **0
and **0°C) for *6,**0 hours.Easily FabricatedHASTELLOY X alloy has
excellent forming and welding characteristics. It can be forged
and, because of its good ductility, can be cold worked. X alloy can
be welded by both manual and automatic methods including shielded
metal arc (covered electrodes), gas tungsten arc (TIG) and gas
metal arc (MIG). The alloy can also be resistance welded.ASME
Boiler and Pressure Vessel CodeHASTELLOY X alloy plate, sheet,
strip, bar, tubing and pipe are covered by ASME specifications
SB***5, SB***2, SB***9, SB***2 and SB***6 under UNS Number
N****2.Heat-TreatmentWrought forms of HASTELLOY X alloy are
furnished in the solution heat-treated condition unless otherwise
specified. X alloy is solution heat-treated at ***0°F (***7°C) and
rapid cooled. Bright annealed products are cooled in
hydrogen.Available in Convenient FormsHASTELLOY X alloy is
available in the form of plate, sheet, strip, billet, bar, wire,
covered electrodes, pipe and tubing, metal powder.Useful for
Aircraft, Furnace and Chemical Process ComponentsX alloy has wide
use in gas turbine engines for combustion zone components such as
transition ducts, combustor cans, spray bars and flame holders as
well as in afterburners, tailpipes and cabin heaters. It is
recommended for use in industrial furnace applications because it
has unusual resistant to oxidizing, reducing and neutral
atmospheres. Furnace rolls of this alloy were still in good
condition after operating for 8,**0 hours at ***0°F (***7°C).
HASTELLOY X alloy is also used in the chemical process industry for
retorts, muffles, catalyst support grids, furnace baffles, tubing
for pyrolysis operations and flash drier components.For more
technical data please contact our service.