Lithium Triborate ( LiB3O5, LBO) Crystal, nonlinear crystal

详情

· Advantages of LBO：

· Broad transparency ranges from **0nm to ***0nm.

· High optical homogeneity (dn≈***6/cm) with little inclusion;

· Relatively large effective SHG coefficient (about three times than that of KDP);

· High damage threshold;

· Wide acceptance angle and small walk-off;

· Type I and type II non-critical phase matching (NCPM) in a wide wavelength range;

· Spectral NCPM about ***0nm.

· Basic properties

· Transparency Range *******0nm

· SHG Phase Matchable Range **1 ~ ***0nm (Type I) *******0nm (Type II)

· Thermal-optic Coefficient

· (°C, λ in μm) dnx/dT=*9.3X***6

· dny/dT=**3.6X***6

· dnz/dT=(*6.**2.1λ)X***6

· Absorption Coefficient <0.1%/cm at ***4nm <0.3%/cm at **2nm

· Angle Acceptance 6.*4mrad-cm (φ, Type I,***4 SHG)

· *5.*7mrad-cm (q, Type II,***4 SHG)

· Temperature Acceptance 4.7°C-cm (Type I, ***4 SHG)

· 7.5°C-cm (Type II,***4 SHG)

· Spectral Acceptance 1.0nm-cm (Type I, ***4 SHG)

· 1.3nm-cm (Type II,***4 SHG)

· Walk-off Angle 0.*0° (Type I ***4 SHG)

· 0.*2° (Type II ***4 SHG)

· NLO Coefficients deff(I)=d*2cosΦ (Type I in XY plane)

· deff(I)=d*1cos2θ+d*2sin2θ (Type I in XZ plane)

· deff(II)=d*1cosθ (Type II in YZ plane)

· deff(II)=d*1cos2θ+d*2sin2θ (Type II in XZ plane)

· Non-vanished NLO susceptibilities d*1=1.*5 ± 0.*9 pm/V

· d*2= *0.*8 ± 0.*9 pm/V

· d*3=0.*5 ± 0.**6 pm/V

· Sellmeier Equations(λ in μm) nx2=2.*****0*0.*****9/(λ**0.*****0)*0.*****1λ**6.*0x***5λ4

· ny2=2.*****0*0.*****1/(λ**0.*****3)*0.*****0λ2*2.0x***4λ4

· nz2=2.*****9*0.*****9/(λ**0.*****3)*0.*****8λ**2.*6x***4λ4

· Technical parameters:

· Flatness λ

· Parallelism < *0 arc sec

· Perpendicularity < 5 arc min

· Angle tolerance < *0 arc min

· Aperture tolerance ± 0.1 mm

· Surface quality *0/5 scratch & dig per MIL-O*****0A

· Clear aperture *0% of full aperture