The iron-based copper-clad laminate has excellent flame retardant
ability, high mechanical strength, dimensional stability, etc.It is
completely designed and manufactured by our company and owns
spectacular characteristics and functions.The material for the base
is from special steel, silicon steel, etc. It has all the functions
as metal material and the following particular characteristics:
High mechanic strength;
Vacancy area convenient for further machinery, procuring and
fixing of the base;
Silicon-steel is iron-magnetic and can be applied on
micro-motors such as VTR, FDD.
Note:
Chaoshun specially produces Metal -based Copper-clad Laminates and
our products have been compiled series with complete
specifications.
Type and specification of Iron-based laminates:CFAF**1, CFAF***-A,
CFAF**5, etc.
The thickness of the iron:0.5mm, 0.8mm, 1.0mm
The thickness of the copper:1oz, 2oz, 3oz, 4oz
Base size:**0mm×**0mm (*3"×*5"); **0mm×**0mm (*0"×*4"); **3mm×**0mm
(*3"×*0")
Test Base:
Thickness of the copper: *5um
Thickness of iron base: 0.5mm
Test Result:
| Item |
Test Item |
Unit |
Test Result |
| 1 |
Peel Strength |
A |
N/mm |
2.3 |
| After Thermal Stress (**0℃) |
N/mm |
2.0 |
| 2 |
Blister Test After Thermal Stress (**0℃, 2min) |
/ |
No Delaminating |
| 3 |
Thermal Resistance |
℃/W |
1.1 |
| 4 |
Flammability (A) |
/ |
FV*0 |
| 5 |
Surface Resistivity |
A |
MΩ |
6.7×**6 |
| Constant Humidity Treatment(*0℃, *5℃, *6h) |
MΩ |
6.7×**6 |
| 6 |
Volume Resistivity |
A |
MΩ·m |
3.2×**7 |
| (*0℃, *5℃, *6h) |
MΩ·m |
3.2×**7/td> |
| 7 |
Dielectric Breakdown (AC) |
KV/MM |
4 |
| 8 |
Dielectric Constant (*0℃, *0%, *6h) |
/ |
4.2 |
| 9 |
Dielectric Dissipation Factor (*0℃, *0%, *6h) |
/ |
0.**7 |