Test
|
BR***0
|
BR***3
|
|
|
Volatile matter?%
max
|
0.*5
|
0.*5
|
|
|
Ash content?%
max
|
0.3
|
0.2
|
|
|
Mooney viscosity of rubber
,ML***1*4?
|
*5
|
*7
|
|
|
Mooney viscosity of rubber
compound ML***1*4??
|
*8
|
*0
|
|
|
**0% stress at definite
elongation,MPa
|
*5min
|
8.5
|
9.4
|
|
*5min
|
9
|
9.6
|
|
|
*0min
|
8.8
|
9.3
|
|
|
Tensile strength, MPa*5min
,min
|
*4.2
|
*5.2
|
|
|
Elongation ?% *5min
,min
|
**0
|
**0
|
|
|
Characters
|
High elastic ,hysteresis loss and small heating , low
temperature filling and membrane fluidity are good , abrasion
resistance and resistance to flexion bending performance are
great.
�
|
Be of ood processing performance , it is easy to be
mixed with various additives to shorten the mixing time and to
reduce tire hysteresis loss and endogenous heat in order to improve
the resisting slippery
of tire.
|
|
|
Usage
|
It is used to produce tire,
sebific duct,rubber belt, seal ring,sole and other rubber
products
|