HX***5 Polyamide Velours Tape
Application: HX***5 is preferably used for cable harnessing in the
automotive industry, It is suitable for sophisticated applications
and is especially applied wherever high noise reduction and high
resistance against abrasion is necessary. The high quality
acrylate_based adhesive offers very good heat and media resistance
and shows an excellent ageing resistance.
Properties Dimension Values Test Method
Thickness mm 1.7 ASTM D***0
Width mm *9.0 ASTM D***0
Adhesion Strength N/cm 1.5 ASTM D***0
Tensile Strength N/cm **0 ASTM D***0
Elongation % *0 ASTM D***0
Temperature Range **0/***0 VW****0
Abrasion resistance strokes >***0
Structure: Non-woven and non-rotting polyester staple fleece,
non-abrasive and soft in combination with an ageing stable and
strong synthetic rubber_based adhesive. *-
Shelf life: *2months is the original package at *3 degree and *5%
relative humidity.
HX***1 Polyester Fleece Tape
Application HX***1 is preferably used for cable harnessing in the
automotive industry, Because of its resistance and soft backing,
HX***1 is suitable for sophisticated in the interior of a car,
HX***1 also suppresses noise because of its soft backing.
Properties Dimension Values Test Method
Thickness mm 0.*0 ASTM D***0
Width mm *9.0 ASTM D***0
Adhesion N/cm 2.5 ASTM D***0
Tensile N/cm *5 ASTM D***0
Elongation % *0 ASTM D***0
Temperature Range **0/***5 VW****0
Unwinding force
Machine processing N/ cm 2.5 ASTM D***0
Structure: Non-woven and non-rotting polyester staple fleece,
non-abrasive and soft in combination with an ageing stable and
strong synthetic rubber_based adhesive.
Shelf life: *2months is the original package at *3degree and *5%
relative humidity.
HX***0 Polyester Fabric Tape
Application: HX***0 is especially suitable for the taping of cable
harness. You will obtain a smooth and durable flexible cable
harness with overlapping bandaging as with spiral bandaging.
Properties Dimension Values Test Method
Thickness mm 0.*5 ASTM D***0
Width mm *9.0 ASTM D***0
Adhesion Strength N/cm 2.5 ASTM D***0
Tensile Strength N/cm *5 ASTM D***0
Elongation % *5 ASTM D***0
Temperature Range **0/***5 VW****0
Unwinding force
Machine processing N/*9mm 2.5 ASTM D***0
Colour: Black
Structure: High quality viscose fabric tape in combination a strong
synthetic rubber_based adhesive.
Shelf life: *2months is the original package at *3degree and *5%
relative humidity.
HX***3 Polyester Fabric Tape
Application: HX***3 is especially designed for cable harnessing in
the automotive industry, Because of the high temperature stability,
the extremely robust backing and the excellent media resistance, it
is ideal for use in the engine area.
Properties Dimension Values Test Method
Thickness mm 0.*5 ASTM D***0
Width mm *9.0 ASTM D***0
Adhesion Strength N/cm 1.5 ASTM D***0
Tensile Strength N/cm **0 ASTM D***0
Elongation % *0 ASTM D***0
Temperature Range **0/***0 VW****0
Unwinding force
Machine processing N/ cm 2.6 ASTM D***0
Structure: High quality polyester fabric of high media resistance,
in combination with a strong, acrylate_based adhesive.
Shelf life: *2months is the original package at *3 degree and *5%
relative humidity.
HX***3A Polyester Fabric Tape
Application: HX***3A is especially designed for cable harnessing in
the automotive industry, Because of the high temperature stability,
the extremely robust backing and the excellent media resistance, it
is ideal for use in the engine area.
Properties Dimension Values Test Method
Thickness mm 0.*8 ASTM D***0
Width mm *9.0 ASTM D***0
Adhesion Strength N/cm 1.5 ASTM D***0
Tensile Strength N/cm **0 ASTM D***0
Elongation % *0 ASTM D***0
Temperature Range **0/***5 VW****0
Unwinding force
**-machine processing N/ cm 2.5 ASTM D***0
Structure: High quality polyester fabric of high media resistance,
in combination with a strong, acrylate_based adhesive.