Aluminum and Titanium base agglomerated flux for Sub ARC Welding

详情

Agglomerated flux SJ**1  
Executive Standard:   GB/T ********9 F5A*-H*8MnA
(Equivalent to: AWS A5.*7. F7A*-EM*2K ); FA

CHARACTERISTICS & FIELD OF USE:   
The flux SJ**1 is a type of aluminum and titanium base agglomerated flux, the basicity of which is 0.5 to 0.8 (acidic). The aluminum and titanium basic type and designed for making the steel pipe and welding general structural steels; pressure vessel & pipe steel & fine grain structural steels. Combination with welding wire H*8MnA & H*8MnMoA.

-The welding flux SJ**1 is characterized by its low Si & moderate Mn pickup & is suitable for single & multi-wire welding as well as for welding by the two-run technique.

-It can be used on DC(+) or AC up to ***0 A. Its good welding characteristics allow it to be used for fillet welding & for welding at high speeds.   

Aluminate and Titanium- basic type / Classification of Flux:  
DIN ****2 : B AB 1 *7 AC *0 M;  
EN **0 : A AB 1 *7 AC; 

MAIN CHEMICAL COMPONENT %:                         
SiO2+TiO2: ~*3 %;   Al2O3+MnO: ~ *4 %;   CaO+MgO: **- %;    CaF2+Feo: ~*0%; 

TYPICAL MECHANICAL PROPERTIES OF ALL WELD METAL
 ( AS WELDED CONDITION ):
SAW WIRE S2; Yield Strength N/mm2> **0    Tensile Strenght N/mm***0 - **0,
Elongation L0=5d0 %> *2,    Impact Energy ISO-V (JOULE) **0°C > *5;

SAW WIRE S2Mo; Yield Strength N/mm2> **0, Tensile Strenght N/mm***0 - **0,
Elongation L0=5d0 %> *8,  Impact Energy ISO-V (JOULE) **0°C > *5;
PACKAGING:     Each *5 KGs/paper bags with P.E inner bag.  
Grain Size: 0.2 ~ 2 mm;  Density: 1.2 Kg/dm3 ;    Basicity (BONISZWSKI) : ~ 1.0; 
INSTRUCTIONS OF USAGE:     
If stored properly, the flux can be used directly from the bag. Flux that has become moist should be re dried for around 2hours at ******0°C prior to use