6CrW2Si

详情

6CrW2Si 

1. Different standards and  Chemical Analysis (%):

Standard	Grade	C	Cr	W	Si	Mn	V	P≤	S≤	Ni	Cu
GB	6CrW2Si	0.55-0.65	1.00-1.30	2.20-2.70	0.50-0.80	≤0.40	__	0.030	0.030	—	0.30
JIS	SKS4	045-0.55	0.50-1.00	0.50-1.00	≤0.35	≤0.35	__	0.030	0.030	0.25	0.25
ASTM	S1	0.40-0.55	1.00-1.80	1.50-3.00	0.15-1.20	0.10-0.40	0.10-0.30	0.030	0.030	0.75
DIN	1.2550	0.55-0.65	0.90-1.20	1.70-2.20	0.70-1.00	0.15-0.4

 

1. Performance and application

 
①Suitable for low-deformation steel and Cr12 series steel that are made of carbon steel with insufficient load-bearing capacity,
and are made of oil-quenched steel, which are prone to brittleness, but are made of high-speed steel or high-strength steel, and
are uneconomical and high-wear molds.
 
②This steel can be used when the main failure mode is wear and collapse.
 
③Suitable for manufacturing scissors, slicing punches, etc.
 
④It can be used for punching dies, press dies, casting finishing tools, pneumatic chisels, etc. that work under heavy loads.
 
⑤As a hot processing steel, it can produce screws and hot riveting punches.
 
⑥High temperature die-cast light alloy head.
 

• Hot forging die, etc.

 

1. 出厂状态：球化退火，

Delivery state: spheroidizing annealing,

• Black/Peeled/Grined/Turned

1. Ultrasonic test:SEP 1921-84 Class D/d
2. Process:EAF+LF+VD+ESR
3. Shape:Round bar ,Flat
4. Delivery Time:30-35 days
5. Packaging Details: Seaworthy Packing
6. Size:

Round bar:
Plate barThickness(mm) 10-400mm

1.  

length: Max5800mm