Silane crosslinked cable material has excellent elasticity, flexibility and electrical stability, and is mainly used in mining cables, shipboard cables and locomotive cables.
| Property | Unit | Standard value | Typical value | Test Method |
| LF***1HP | ||||
| Hardness | Shore A | *3±2 | GB/T ***1 | |
| Tensile Strength | MPa | �*3 | *0 | GB/T ***0.3 |
| Elongation at Break | % | �**5 | **0 | |
| Impact Brittleness Temperature (**6 ºC ) | - | �*5/*0 | Pass | GB/T ***0 |
| · Thermal Ageing (**5 ºC ***8H) | ||||
| Change Rate of Tensile Strength | % | �±*0 | *8 | GB/T ***1.*2 |
| Change Rate of Elongation at Break | % | �±*0 | *5 | |
| · Thermal Elongation ( **0 ºC, 0.2MPa , *5min) | ||||
| Elongation under The Load | % | �**0 | *5 | GB/T ***0 |
| Elongation after Cooling | % | �5 | 0 | |
| Volume Resistivity *0 ºC | Ω·m | 1**0 *4 | 4.3**0 *4 | GB/T ***0 |
| Dielectric Strength | MV/m | �*5 | *0 | GB/T ***8.1 |
| Dielectric Constant | - | �2.*5 | 2.*8 | GB/T ***9 |
| Dielectric Loss Tangent | - | �1**0 *3 | 2**0 *4 | |
| Gel Content | % | �*0 | *5 | GB/T ****7 |
![Lf-6125-Utj Irradiation Crosslinking LSZH Compounds for Photovoltaic Cable [125 º C] Insulation](https://int.chinacdnb2b.com/p-6176626-20240417021620/lf-6125-utj-irradiation-crosslinking-lszh-compounds-for-photovoltaic-cable-125-acirc-ordm-c-insulation.jpeg "Lf-6125-Utj Irradiation Crosslinking LSZH Compounds for Photovoltaic Cable [125 º C] Insulation")