Damisol@3500LoV

详情

*@******************** component of the low viscosity of Freon resistant epoxy resin
The low of VOC
Is suitable for motor and transformer from low voltage to voltage
The criterion can be applied to any form of impregnation and V (P) I process equipment
The solution of: one three two two zero three for a long time no longer paint
Is for H (UL ***6)
summary
One component solvent-free epoxy resin.
Low viscosity epoxy resin, freon resistant, heat cured with grade H or above the lasting high temperature properties.
application
The impregnated resin is widely used in low-voltage and medium voltage industrial seal motor.
Excellent insulation and mechanical properties at high temperature, but also can be applied to the traction motors and transformers.
Operation process
Mainly used for atmospheric pressure or vacuum pressure impregnation process.
Due to the special reaction, this product can be used in any form of hot dip process (atmospheric pressure immersion, dip or dipping roll).
In hot dipping process, the motor in the impregnation before preheating at *0 DEG C, gelation and curing process will be completed within 5 hours or **0 DEG C within 2 hours under the condition of **0 DEG C (test temperature of copper wire).
Set the curing process depends on the operation of the oven parameters can be optimized in the letter technical team supported by this process.
packing
*0kg.
**0kg barrel
storage environment
Below *5 degrees Celsius, valid for up to *2 months. High temperature will lead to shorten the storage period.
Such as resin stored in large storage tank, recommended to keep under standard pressure in dry air or nitrogen.
health and safety
Avoid contact with skin and eyes.
Wear safety gloves and eye during operation.
Unit specification reference standard
physical property
Slight odor
Appearance pale yellow
The flash point is greater than or equal to **0 DEG C
Viscosity (Brookfield, *3 C) mPas **0 + **0
Gel time (**0 degrees C) min *2 + 3 Gelnorm, *0g
Tg C **2 IEC ****6
VOC% ISO < 2 ******3
Mechanical properties
The bond strength (*3 C) daN *4 IEC ***3
The bond strength (**0 C) daN *3.8 IEC ***3
The bond strength (**5 C) daN *0 IEC ***3
The bond strength (**0 C) daN 8.3 IEC ***3
Chemical properties
Transformer oil resistant% < 0.1 ISO **5
Absorbent (*3 DEG, *4 hours)% less than 0.3 ISO *2 (Method 1)
Water absorption (7 days *3 C)% less than 1 ISO *2 (Method 1)
Chemical resistance (*0% HCl%) less than 0.*4 ISO **5
Electrical performance
The insulation strength (*0% R.H, *3oC) kV/mm **9 DIN ****8 / VDE ***0
The insulation strength (*2% R.H, *3oC, *6 hours) kV / mm **3 DIN ****8 / VDE ***0
Loss factor (*5 C, tangent% < 1 IEC****0)
Loss factor (**5 DEG C, tangent)% less than or equal to 2 IEC ****0
Loss factor (**0 DEG C, tangent)% less than or equal to 5.5 IEC ****0