Water Based Dacromet Coating Paint JH-9382 Water Based Dacromet Coating Paint JH-9382 Water Based Dacromet Coating Paint JH-9382 Water Based Dacromet Coating Paint JH-9382
Next

Water Based Dacromet Coating Paint JH-9382

离岸价格

获取最新报价

( Negotiable )

|

40 Kilogram Minimum Order

国家:

China

型号:

JH-9382

离岸价格:

( Negotiable ) 获取最新报价

位置:

CHINA

最小订单价格:

-

最小订单:

40 Kilogram

包装细节:

Pack A:16kg/ Metal Barrel Pack B:24KG Plastic Barrel

交货时间:

Ten days after receipt of advance payment

供应能力:

2 Ton per Day

付款方式:

T/T, L/C, Other

產品組 :

现在联系

联系人 Jiang

Changzhou, Jiangsu

现在联系

产品规格

  • Other Names: zinc flake coating paint
  • Main Raw Material: Acrylic
  • Usage: Appliance Paint
  • Application Method: Spray
  • State: Liquid Coating
  • Brand Name: JUNHE
  • Viscosity:According to operating demand.
  • Operating temperature:20±2â
  • Cr6+:â¥25g/L
  • Color:Silver
  • Coating method:Dip Spin & Spraying

详情

Minimum Order Quantity: **0 Kilograms
Packaging Details: Pack A:*6kg/ Metal Barrel
                               Pack B:*4KG Plastic Barrel
                               Pack C:Based on the amount of B agent A

Delivery Time: Ten days after receipt of advance payment
Supply Ability: 2 Tons per Day
Coating Method: Dip Spin & Spray
Color: Silver
PH: 3.**5.2
Specific Gravity: 1.*3±0.*5( Spraying)1.*3±0.*5(dip-spin Coating)
Viscosity: According To Operating Demand.
Operating Temperature: *0±2℃
Description:

 

JH****2 is made up of three packs: A,B and C;
Pack A: It is silver gray slurry that mainly chemically combined with super fine flake Zn, super fine flake Al and organic additive.
Pack B: It is water solution that mainly combined with corrosion protecion additive, particular regulator water solution etc.
Pack C: It is the tackifier of the coating which mainly made up of cellulose white or yellowish powder.

 

Performance characteristics:

 

The film is silver white, good surface finish, high corrosion resistance, good coating.
Coating Process:

 

1. Mix Ratio
Pack A:*6.0 kg
Pack B:*4.0 kg (the quantity can be increased appropriately if spray coating)
Pack C:***0 g (according to different viscosity demand )

 

2. Before Mixture, Keep weighted A&B into the water bath at *5±2℃ , then stir A to make metal slurry disperse uniformly by frequency mixer ,after A is fully evenly dispersed, reduce the agitating speed to *0r/min, and add B.
Add B to the stirring A slowly. At the moment, the barrel temperature will go up, when it reaches *5℃, startup refrigerating device to keep the barrel temperature constant at *5℃.

 

3.Add B to the stirring A slowly. At the moment ,the barrel temperature will go up,when it reaches *5℃, startup refrigerating device to keep the barrel temperature constant at *5℃.

 

4. Stir the mixture about 1~2 hours fast after B added, then add C. C should be powdered if lump exist.(The barrel temperature should not be lower than *0℃, otherwise C will not be dissolved sufficiently .)Then stir *2 hours continuously.

 

5. The coating should be filtrated by **0 mesh stainless steel screen before pouring into dip barrel.

 

6. Temperature control device should be equipped with dip barrel to keep the temperature of coating at *2±2℃.
(If temp. is too high, the paint is liable to deteriorate, and viscosity will be effected.) The coating should be stirred circularly to keep evenly dispersed.

 

7. Test density, PH, Temperature, Viscosity and Cr6+ content of coating every 8 hours if operate continuously.
Attentions:

 

Other chemicals such as any kinds of acid, alkali salt can not be mixed into coating, for these can activate Zn & Al plate to aging the coating.

 

Avoid irradiation of sunshine and ultraviolet ray for long time when operating, otherwise it will accelerate aging or polymerization of the coating .

 

It is very important to control the temperature of coating. If the temperature of coating changes when operating, it will effect the viscosity, then effec the coating quatity on workpiece. So the relations among temperature, viscosity and spinning process shoud be controlled well when coating.

 

The viscosity will be different if coating method is different. Choose low data if spray coating,and choose high data if dip spin coating.

Technical data:

 

No. Item Data
1 Color Silver
2 Coating method Dip Spin & Spraying
3 PH 3.**5.2
4 Cr6+ ≥*5g/L
5 Specific gravity 1.*3±0.*5( spraying)1.*3±0.*5(dip-spin coating)
6 Viscosity According to operating demand.
7 Operating temperature *0±2℃

国家: China
型号: JH-9382
离岸价格: ( Negotiable ) 获取最新报价
位置: CHINA
最小订单价格: -
最小订单: 40 Kilogram
包装细节: Pack A:16kg/ Metal Barrel Pack B:24KG Plastic Barrel
交货时间: Ten days after receipt of advance payment
供应能力: 2 Ton per Day
付款方式: T/T, L/C, Other
產品組 : dacromet coating
Water Based Dacromet Coating Paint JH-9382
Water Based Dacromet Coating Paint JH-9382
Water Based Dacromet Coating Paint JH-9382
Water Based Dacromet Coating Paint JH-9382